7 way 12/8 mm HDPE Microduct Tube
7 ways
Design
- A bundle of micro- or mini-tubes (strengthened wall size) is surrounded by single thin HDPE sheath. The design makes the duct assemblies suitable for installation in other existing ducts. The micro ducts are optimized for best cable blowing performance. - The inner micro duct has suitable low friction characteristics on the inside surface. The micro duct has colors according to figures 1.
Raw materials
HDPE of a high-molecular type with the following parameters is used for production of the Tube Bundle: - Melt flow index: 0.1 ～ 0.4 g/10 minutes EN ISO 1133 (190 °C, 2.16 KG) - Density: Min. 0.940 g/cm3 ISO 1183 - Tensile strength at yield: Min. 20MPa ISO 527 - Elongation at the break: Min 350% ISO 527 - Environmental stress crack resist (F50) Min. 96 hours ISO 4599
Construction
- PE sheath: The outer sheath is manufactured from colored HDPE, halogen free. Normal outer sheath color is orange. Other color is possible upon customer request. - Micro duct: The micro duct is manufactured from HDPE, extruded from 100% virgin material. The color shall be red, green, blue, white or other customized.
|
Pos.
|
Mechanical performance
|
Test conditions
|
Performance
|
Standard
|
|
1
|
Tensile strength
at yield |
Rate of extension:
100mm/min |
≥1200N
|
IEC 60794-1-2
Method E1 |
|
2
|
Crush
|
Sample length: 250mm
Load: 1680N Duration of Max. load: 1 minutes Recovery time: 1 hour |
The outer and inner diameter shall show, under visual examination without damage and no reduction of diameter greater than 15%.
|
IEC 60794-1-2
Method E3 |
|
3
|
Kink
|
≤120mm
|
-
|
IEC 60794-1-2
Method E10 |
|
4
|
Impact
|
Striking surface radius: 10mm
Impact Energy: 1J Number of impact: 3 times Recovery time: 1 hour |
Under visual examination, there shall be no damage to the micro duct.
|
IEC 60794-1-2
Method E4 |
|
5
|
Bend radius
|
Number of turns: 5
Mandrel diameter: 144mm Mumber of cycles: 3 |
The outer and inner diameter shall show, under visual examination without damage and no reduction of diameter greater than 15%.
|
IEC 60794-1-2
Method E11 |
|
6
|
Friction
|
/
|
≤0.1
|
FCST
|
|
Pos
|
Item
|
Specification
|
|
|
1
|
Appearance
|
Smooth outer wall (UV-stabilized) without visible impurities; well-proportioned color, no bubbles or cracks; with defined markings
on outer wall. |
|
|
2
|
Tensile strength
|
Use Pull socks to tension a sample in accordance with table below:
Sample length: 1m Tensile speed: 20mm/min Load: 5400N Duration of the tension: 5 min. |
No visual damage or residual deformation greater than 15% of the duct assembly outer diameter.
|
|
3
|
Crush Resistance
|
A 250mm sample after 1 minute load time and 1 hour recovery time. Load (plate) shall be 2000N. The imprint of the plate on the
sheath is not considered as mechanical damage. |
No visual damage or residual deformation greater than 15% of the duct assembly outer diameter.
|
|
Pos
|
Item
|
Specification
|
|
|
4
|
Impact
|
Striking surface radius shall be 10mm and impact energy 10J. Recovery time shall be one out. The imprint of the striking surface
on the microduct is not considered as mechanical damage. |
No visual damage or residual deformation greater than 15% of the duct assembly outer diameter.
|
|
5
|
Bend
|
Diameter of mandrel shall be 40X OD of sample, 4 turns, 3 cycles.
|
No visual damage or residual deformation greater than 15% of the duct assembly outer diameter.
|
Completed packages of the HDPE Tube Bundle on drums can be stored outdoor max. 6 months upon the date of production. Storage temperature: -40°C ～ +70°C Installation temperature: -30°C ～ +50°C Operating temperature: -40°C ～ +70°C
7 ways
Design
- A bundle of micro- or mini-tubes (strengthened wall size) is surrounded by single thin HDPE sheath. The design makes the duct assemblies suitable for installation in other existing ducts. The micro ducts are optimized for best cable blowing performance. - The inner micro duct has suitable low friction characteristics on the inside surface. The micro duct has colors according to figures 1.
Raw materials
HDPE of a high-molecular type with the following parameters is used for production of the Tube Bundle: - Melt flow index: 0.1 ～ 0.4 g/10 minutes EN ISO 1133 (190 °C, 2.16 KG) - Density: Min. 0.940 g/cm3 ISO 1183 - Tensile strength at yield: Min. 20MPa ISO 527 - Elongation at the break: Min 350% ISO 527 - Environmental stress crack resist (F50) Min. 96 hours ISO 4599
Construction
- PE sheath: The outer sheath is manufactured from colored HDPE, halogen free. Normal outer sheath color is orange. Other color is possible upon customer request. - Micro duct: The micro duct is manufactured from HDPE, extruded from 100% virgin material. The color shall be red, green, blue, white or other customized.
|
Pos.
|
Mechanical performance
|
Test conditions
|
Performance
|
Standard
|
|
1
|
Tensile strength
at yield |
Rate of extension:
100mm/min |
≥1200N
|
IEC 60794-1-2
Method E1 |
|
2
|
Crush
|
Sample length: 250mm
Load: 1680N Duration of Max. load: 1 minutes Recovery time: 1 hour |
The outer and inner diameter shall show, under visual examination without damage and no reduction of diameter greater than 15%.
|
IEC 60794-1-2
Method E3 |
|
3
|
Kink
|
≤120mm
|
-
|
IEC 60794-1-2
Method E10 |
|
4
|
Impact
|
Striking surface radius: 10mm
Impact Energy: 1J Number of impact: 3 times Recovery time: 1 hour |
Under visual examination, there shall be no damage to the micro duct.
|
IEC 60794-1-2
Method E4 |
|
5
|
Bend radius
|
Number of turns: 5
Mandrel diameter: 144mm Mumber of cycles: 3 |
The outer and inner diameter shall show, under visual examination without damage and no reduction of diameter greater than 15%.
|
IEC 60794-1-2
Method E11 |
|
6
|
Friction
|
/
|
≤0.1
|
FCST
|
|
Pos
|
Item
|
Specification
|
|
|
1
|
Appearance
|
Smooth outer wall (UV-stabilized) without visible impurities; well-proportioned color, no bubbles or cracks; with defined markings
on outer wall. |
|
|
2
|
Tensile strength
|
Use Pull socks to tension a sample in accordance with table below:
Sample length: 1m Tensile speed: 20mm/min Load: 5400N Duration of the tension: 5 min. |
No visual damage or residual deformation greater than 15% of the duct assembly outer diameter.
|
|
3
|
Crush Resistance
|
A 250mm sample after 1 minute load time and 1 hour recovery time. Load (plate) shall be 2000N. The imprint of the plate on the
sheath is not considered as mechanical damage. |
No visual damage or residual deformation greater than 15% of the duct assembly outer diameter.
|
|
Pos
|
Item
|
Specification
|
|
|
4
|
Impact
|
Striking surface radius shall be 10mm and impact energy 10J. Recovery time shall be one out. The imprint of the striking surface
on the microduct is not considered as mechanical damage. |
No visual damage or residual deformation greater than 15% of the duct assembly outer diameter.
|
|
5
|
Bend
|
Diameter of mandrel shall be 40X OD of sample, 4 turns, 3 cycles.
|
No visual damage or residual deformation greater than 15% of the duct assembly outer diameter.
|
Completed packages of the HDPE Tube Bundle on drums can be stored outdoor max. 6 months upon the date of production. Storage temperature: -40°C ～ +70°C Installation temperature: -30°C ～ +50°C Operating temperature: -40°C ～ +70°C
Essential details
- Model Number:7ways 12/8mm DB Tube Bundle
- Type:Micro Duct & Tube Bundle
- Place of Origin:Wenzhou, China
- Brand Name:ANMASPC
- Use:FTTH, Cable Installation
- Warranty Time:12months
- Network:None
- Sub duct Inner diameter:8mm
- Sub duct outer diameter:12mm
- PE Sheath:1.2mm
- Outer Diameter::38.4mm*35.2mm (±0.5mm)
- Melt flow index:0.1 ~ 0.4 g/10 minutes
- Density:Min. 0.940 g/cm3
- Tensile strength at yield::Min. 20MPa
- Elongation at the break::Min 350%
- Environmental stress crack resist (F50):Min. 96 hours
- Supply Ability1000000 Meter/Meters per Week